Çinko Kaplanmış Yay (SH) Çeliğinin Korozyon Davranışı


Danışman Ş. , Maşlak M.

UDCS'19 Fourth Iron and Steel Syposium, Karabük, Türkiye, 4 - 06 April 2019, ss.304-307

  • Basıldığı Şehir: Karabük
  • Basıldığı Ülke: Türkiye
  • Sayfa Sayısı: ss.304-307

Özet


 Corrosion is an important problem encountered in metals and alloys.
One of the effective solutions to protect against atmospheric corrosion is the electrolytic zinc coating.
In this study, the corrosion behaviour of free cutting (Ç-1080) steel in different thickness of electrolytic zinc plating was investigated using electrochemical methods. 
In these methods, potential ve time change, AC impedance and current – ​​potential curves were taken into account respectively.
Corrosion potential (Ecor), corrosion current (icor) and other corrosion parameters were determined from current-potential curves. 
Steel samples coated in cyanide baths were obtained in thicknesses of 10 µ and 20 µ. Two different processing times were used for this. 
The basic cyanide zinc coating bath was prepared by adding (1 gram per liter of zinc (Zn (CN)2) zinc cyanide, 85 grams (NaOH) sodium hydroxide, 40 grams (NaCN) sodium cyanide and 5 grams zinc brightener (patent)). 
After this coating, samples were passivated by immersion in solution % 20 CrO3 +% 3 H2S04 +% 3 HNO3  for 60 seconds. 

 After the current-potential curves of the coated steel samples were taken in aqueous medium, the change in the composition of the surface was investigated by SEM / EDS and XRD analyzes.
The corrosion behaviour and corrosion rates of coated steel samples in aqueous medium were determined by three different methods. 
As a result, it was shown that the corrosion of 20 µ zinc coated steel samples in neutral environment decreased by 93% after the passivation process.