Synthesis and characterization of oligosalicylaldehyde-based epoxy resins

Sahmetlioglu E., MART H., YURUK H., SURME Y.

CHEMICAL PAPERS-CHEMICKE ZVESTI, cilt.60, sa.1, ss.65-68, 2006 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 60 Sayı: 1
  • Basım Tarihi: 2006
  • Doi Numarası: 10.2478/s11696-006-0012-1
  • Dergi Adı: CHEMICAL PAPERS-CHEMICKE ZVESTI
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.65-68
  • Erciyes Üniversitesi Adresli: Hayır

Özet

The synthesis of a new epoxy resin of oligosalicylaldehyde by the reaction with epichlorohydrin is reported. New resin's epoxy value and chlorine content were determined and found to be 25 % and 1 %, respectively. The characterization of the new resin was instrumented by FTIR, H-1 NMR, scanning electron microscopy, and thermal gravimetric analyses. TGA results showed that the cured epoxy resin has a good resistance to thermal decomposition. The mass losses of cured epoxy resin were found to be 5 %, 10 %, 50 % at 175 degrees C, 240 degrees C and 400 degrees C, respectively. On the curing procedure the resin was cured with polyethylenepolyamine at 25 degrees C for 8 h and 100 degrees C for 1.5 h. The FTIR spectrum of new epoxy resin gave the peak of oxirane ring a (nu) over bar = 918 cm(-1).