Directional solidification of Al-Cu-Ag alloy

---

Atıf İçin Kopyala

Boyuk U., Maraşlı N., Kaya H., Çadırlı E., Keslioglu K.

APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, cilt.95, sa.3, ss.923-932, 2009 (SCI-Expanded)

• Yayın Türü: Makale / Tam Makale
• Cilt numarası: 95 Sayı: 3
• Basım Tarihi: 2009
• Doi Numarası: 10.1007/s00339-009-5130-5
• Dergi Adı: APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING
• Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
• Sayfa Sayıları: ss.923-932
• Erciyes Üniversitesi Adresli: Evet

Özet

Al-Cu-Ag alloy was prepared in a graphite crucible under a vacuum atmosphere. The samples were directionally solidified upwards under an argon atmosphere with different temperature gradients (G=3.99-8.79 K/mm), at a constant growth rate (V=8.30 mu m/s), and with different growth rates (V=1.83-498.25 mu m/s), at a constant gradient (G=8.79 K/mm) by using the Bridgman type directional solidification apparatus. The microstructure of Al-12.80-at.%-Cu-18.10-at.%-Ag alloy seems to be two fibrous and one lamellar structure.