Morphological similarity of a tri-block copolymer processed at ambient and elevated temperatures


Inceoglu S., Aytun T., Menceloglu Y. Z., Ozen İ., Acar M. H.

KOREA-AUSTRALIA RHEOLOGY JOURNAL, cilt.24, sa.4, ss.313-321, 2012 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 24 Sayı: 4
  • Basım Tarihi: 2012
  • Doi Numarası: 10.1007/s13367-012-0038-6
  • Dergi Adı: KOREA-AUSTRALIA RHEOLOGY JOURNAL
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.313-321
  • Erciyes Üniversitesi Adresli: Evet

Özet

We investigated the effect of temperature on the morphology of a tri-block copolymer (BCP) processed in a capillary rheometer. The material used was a polystyrene-b-poly(2-ethylhexyl acrylate)-b-polystyrene (PS-b-PEHA-b-PS) tri-block copolymer, which was synthesized by ATRP with a molecular weight of 38.5 K consisting of 49 molar % PEHA. According to the rheological data obtained with dynamic viscoelastic oscillatory measurements, order-disorder temperature (ODT) of the BCP was measured at around 110A degrees C. Considering this observation, the samples were studied under different temperatures and pressures (from 110A degrees C to 28A degrees C and from 48 to 75 bar) in capillary rheometer. All processed materials were characterized by using differential scanning calorimetry (DSC) and atomic force microscopy (AFM). It was found that all samples processed by aid of either temperature or pressure showed similar mixed morphologies (a mixture of the ordered and disordered structures i.e., the reduction of microphase separation due to processing).